Corrosion of hot-dip-galvanised steel and zinc alloy-coated steel in ammonia and ammonium chloride

There are many potential causes of corrosion in animal buildings. Animals exhale large quantities of moisture into the air creating high relative humidity in the building if the moisture is not properly vented. High humidity increases the potential for condensation. In addition, ammonia may be found in large quantities in animal buildings. Ammonia is released from manure and urine. In addition, ammonium chloride is used as a nitrogen source in fertilisers. In this study, the atmospheric corrosion of hot-dip-galvanised steel and zinc alloy-coated steel such as zinc–aluminium and zinc–aluminium–magnesium has been studied in atmospheres containing different levels of ammonia. Investigations have also been conducted at different levels of ammonium chloride. The results are discussed in view of the mechanisms of corrosion of zinc and zinc alloy-coated steel in ammonia and ammonium chloride-containing environments.     

Investigation of the influence of iron-containing abrasives on the corrosion behaviour of the aluminium alloy AlSi1.2Mg0.4

The corrosion resistance of aluminium surfaces is closely linked to the surface state after a grinding process. For years, iron-containing abrasive materials were suspected to lead to increased corrosion susceptibility after processing of aluminium surfaces. To prove a possible correlation between the iron content of an abrasive and the corrosion behaviour of aluminium components, scientific investigations and experimentally practical corrosion tests are necessary. For the current investigation, specimens of a technical Al-Si alloy from the same batch were used. The test specimens were mechanically ground with various resin-bonded model abrasives containing different iron contents. The performed corrosion tests did not reveal a negative influence of the different iron-containing abrasives on the corrosion behaviour of the Al–Si alloy. However, the most sensitive measuring method (electrochemical noise) showed differences in the surface activity depending on the type of abrasive.     

Process and joint quality of ultrasonic vibration enhanced friction stir lap welding

In order to improve the process effectiveness and joint quality, ultrasonic vibrations were integrated with friction stir lap welding. Effect of ultrasonic exertion on the process and joint quality of AA 6061-T6 were investigated. Upon ultrasonic exertion, joints owned larger effective lap width, shorter hooks and improved strength. Weld fracture mode changed from a ductile–brittle mixed mode to a more ductile mode while the fracture path shifted from lap interface to beyond the stir zone. Material flow and interface defects were characterised using lap welded dissimilar aluminium alloy joints. Ultrasonic vibration improved the material flow and reduced the interfacial defects. Variations in failure load of joints were found in accordance with the variations in material flow and interfacial defects.     

Corrosion behaviour of AA2024 aluminium alloy in different tempers in NaCl solution and with the CeCl3 corrosion inhibitor

The paper analyses the corrosion behaviour of naturally and artificially aged AA2024 alloy in NaCl solution and in the presence of an environment-friendly corrosion inhibitor, CeCl₃. On the basis of the values of polarisation resistance and corrosion current density, the corrosion resistance of the protective inhibitor film is established as well as the general corrosion resistance of this aluminium alloy. Resistance to pit formation is determined based on the difference in pitting and corrosion potentials while resistance to pit growth is determined based on the amount of charge consumed during pit growth. A scanning electron microscope is used to examine the morphology of the pits formed during the pitting corrosion testing, as well as to determine the cerium content on intermetallic particles and the matrix AA2024 alloy. The corrosion behaviour of AA2024 alloy is investigated after different test periods in NaCl solution and in the same solution with the CeCl₃ inhibitor. The corrosion resistance of both tempers of AA2024 alloy is more than one order of magnitude higher in the presence of CeCl₃. An explanation of the observed differences in the corrosion behaviour of the naturally and artificially aged AA2024 alloy is proposed. Different corrosion behaviour of the alloy after different test periods is also explained.     

雕刻技术的研制和应用

在对铝合金铸件进行X射线实时探伤时，由于采集回来的许多图像的目标物体的轮廓比较模糊，这样在评片时容易造成对铸件的误判和漏判。针对这种现象并结合这类图像噪声源多的特点，在研究常用卷积算法的基础上，采用特殊卷积（特殊的卷积核）操作，同时根据雕刻的艺术底色为灰色，最后给卷积结果加上灰度值128，实验结果表明图像中目标物体的轮廓变得更清楚，同时处理后的图像具有比较好的三维效果，这给工作人员在看图时带来了方便。     

垂直磁记录介质薄膜研制的新途径(英文)

本文阐述了铝氧化电沉积法获得磁记录材料的基本原理,研究了铝交流氧化膜中沉积磁性金属及其合金制备垂直磁记录薄膜的新途径,建立了铝交流氧化电沉积法,探讨了氧化膜的结构和磁特性的关系。     

Grain Boundary Sliding in Fatigue of Pure Aluminum

The distributions of plastic strain near grain boundaries induced by fatigue loading were investigatedby the fiducial grid method in pure aluminum specimens, and the resulted grain boundary sliding(GBS) was systematically analysed. The results show that the strain field near a grain boundary isnonuniform. GBS is restricted by the junction of grain boundaries and causes discontinuities of bothdisplacement and strain. A peak value of shear strain was created in short-range area across the grainboundary. GBS plays an important role in cyclic softening and secondary hardening. The control fac-tor of GBS is the relative orientation between two grains and the macro orientation of the grainboundary rather than the ∑ value of the boundary.     

5754-H34铝合金板材生产工艺研究

研究了不同冷变形程度，退火温度对5754铝合金冷轧板材的组织和力学性能的影响，确定了5754合金H34状态板材的生产工艺参数，即冷变形程度25%-45￥，稳定化退火温度120-160℃，保温时间3-6h，在工业生产条件下，其产品的技术指标达到了用户要求。     

超大型材生产经验

对几种超大型材挤压生产的工艺技术、工模具设计、挤压参数控制等过程进行了分析，通过例子总结了挤压生产超大型材的经验及关键技术。     

浅析6063铝型材表面“铝丝印”的成因与对策

在介绍“铝丝印”概念的基础上，从金属腐蚀学的观点出发，分析了“铝丝印”形成的电化学腐蚀机理，并提出了具体的解决措施。